Scientific Reports volume 13, Article number: 13365 (2023) Cite this article 287 Accesses 1 Altmetric Metrics details Water pollution from synthetic dyes and oil spills has a significant impact on the

Scientific Reports volume 13, Article number: 13365 (2023) Cite this article

287 Accesses

1 Altmetric

Metrics details

Water pollution from synthetic dyes and oil spills has a significant impact on the environment and living species. Here, we developed a low-cost, environmentally friendly and easily biodegradable magnetic hybrid bio-sponge nanocomposite from renewable resources such as collagen and cellulose (Kenaf fibre cellulose–collagen, KFCC). We loaded it with magnetic bimetallic Fe3O4@TiO2 (BFT) NPs to produce a photocatalyst material (KFCC-BFT) for the treatment of colored wastewater as well as a sorbent for oil–water separation. The characterization of the bimetallic BFT NPs by XRD, HRTEM and VSM showed the deposition of TiO2 particles onto the surface of Fe3O4 with lattice interlayers spacing of 0.24 and 0.33 nm for Fe3O4 and TiO2, respectively with ferromagnetic property. The UV–vis diffuse reflectance spectra result indicated that the band gap energy of bio-sponges decreases with the increase of the bimetallic moiety. The photocatalytic efficiency of the as-prepared magnetic hybrid bio-sponge in the degradation of crystal violet dye was up to 91.2% under visible light conditions and 86.6% under direct sunlight exposure. Furthermore, the magnetic hybrid bio-sponge was used to separate motor oil from water (> 99%) and had a high oil sorption capacity of 46.1 g/g. Investigation of the recyclability and reusability performance for 9 cycles revealed that the bio-sponge had a high sorption capacity for up to 5 cycles. Our results suggest that the bio-polymer-supported BFT hybrid nanocomposite is a cost-effective and easily biodegradable photocatalyst and has great potential for real-field environmental remediation applications.

Environmental pollution, predominantly water pollution, is currently a major global threat imposing severe hazards to both human and ecosystem health. Water pollution is a severe concern for all stakeholders including society, public authorities, and industries1. The rapid development of industries such as textile, leather, paint, paper, printing, and plastic as well as offshore oil and gas leads to the increase in the discharge of various pollutants into water2. One of the most common pollutants are organic pollutants such as organic dyes, agrochemicals, phenols, cosmetics, pharmaceutical and petrochemical wastes, which are very hazardous to aquatic organisms and damaging whole ecosystems due to the reduction of the amount of dissolved oxygen in the water in their oxidative decomposition process3,4. Amongst various organic pollutants, soluble dyes and insoluble oils are causing severe damage to the ecosystem. Synthetic dyes are the most used in industries and are composed of polyaromatic molecules containing one or more azo bonds N=N–) that give permanent color to materials. The application of synthetic dyes is diverse ranging from textile and paint to leather industries5,6,7. The unused synthetic dyes present in water are toxic, carcinogenic, and mutagenic and may affect the aquatic environment and human beings, even at a low-level concentration5,6. It is challenging to completely remove colour pollutants from water using traditional wastewater treatment techniques such as absorption and oxidation8,9.

In general, effluents containing soluble contaminants, solids, colloids, organic matter and minerals are removed through various physical, chemical and/or biological techniques10. For the removal of organic contaminants from contaminated effluents, conventional water treatment techniques such as air flotation, precipitation, coagulation, oxidation, adsorption, ion exchange, membrane filtration, etc., are popular11,12. Each treatment method has its own advantages and limitations such as operational costs, efficiency, functionality, dependability, eco impression, post-treatment requirements, and also the creation of sludge and toxic by-products. For intense, photocatalytic degradation has been considered an effective and advanced approach to removing the dyes from the wastewater owing to its advantages such as low cost, non-selective degradation and operating with conventional separation technology without further secondary pollution13. Among different semiconductor photocatalysts developed for the removal of organic contaminants in wastewater, TiO2 nanoparticles (NPs) have been extensively used owing to non-toxicity, low cost and availability, excellent chemical and thermal stability, high catalytic activity, and excellent carrier properties14,15,16. However, the TiO2 NPs have some drawbacks that restrict their real field uses as photocatalysts for wastewater treatment, including agglomeration, the high recombination rate of photo-generated electron–hole pairs and tough recovering due to smaller particle sizes17,18,19. Moreover, the intrinsic large bandgap energy (3.23 eV) limits the use of TiO2 NPs for solar irradiation applications20. Bimetallic Fe3O4@TiO2 (BFT) NPs have been extensively investigated to overcome the separation or recovery problem of TiO221. Magnetic Fe3O4 NPs based photocatalysts provide a real field practicable method to recover magnetic particles from the reaction media as well as possible reuse of the catalyst. Additionally, magnetic Fe3O4 NPs have superior magnetism, excellent compatibility, low cytotoxicity despite high loading and can speed up the transfer of photo-induced electrons between (Fe3+, Fe2+) to increase the photocatalytic activity of TiO222,23.

Water pollution by oil spills can happen during the process of offshore activity by accidents involving tankers, barges, pipelines, refineries, drilling operations, and storage facilities. Oil spills in water bodies not only destroyed aquatic organisms such as sea birds, mammals, algae, etc. but the sand on the coastline was also severely polluted. Following a large oil spill, the effects on ecosystems and economies can last for decades, making the problem of oil/water separation a global challenge24,25,26,27. Several methods can be used to control and eradicate oil leaks from water such as oil bloom or containment bloom, which is a temporary floating barrier method used to contain oil, a skimmer using skimming agents to skim oil from the surface of the water, in situ burning to fire away oil slicks at the surface of the water, chemical dispersants to break the emulsion oil/water and physical sorbents to absorb oil. Among the aforementioned methods for oil/water separation, physical sorbents have gained special attention amongst researchers and industry communities owing to their low density, high 3D porous material (sponges or aerogels), large surface area, surface roughness, tortuosity, recyclability, complete removal and absence of secondary pollution28,29,30,31. Hence, an effective photocatalytic method for the removal of both dyes and oils from wastewater is ideally required.

In recent years, native cellulose and naturally derived nano cellulose have been extremely used in research as renewable and sustainable materials for the preparation of sorbent sponges suitable for the photodegradation of organic pollutants and oil/water emulsion separation. Due to its numerous beneficial features such as renewability, biodegradability, lightweight, large surface area, good mechanical strength, thermal stability and non-toxicity, extracted cellulose from the lignocellulosic fiber is frequently used as filler or reinforcing material for the preparation of composites, paper and textile industries, automobiles and 3D scaffold biomaterials. Super-hydrophobic and super-hydrophilic/super-oleophobic cellulose sponges have been fabricated for oil/water separation26,28,29. In the same trend of preparing bio-based advanced materials, collagen which is a by-product waste from the leather industry has been recently used for the preparation of sorbent sponges for wastewater treatment. Collagen-based biomaterials have been prepared for various applications including scaffolds for tissue engineering32,33,34 bioengineered scaffolds for scarless healing of deep burns35, conducting hybrid aerogels36, and water remediation6 due to its wide availability, high biocompatibility and biodegradability. Each year, a huge amount of collagen-containing waste is disposed into the environment from leather industries, therefore, preparing environmentally free and cost-effective bio-based materials from leather waste is highly feasible and viable.

Herein, a hybrid nanocomposite comprising cellulose and collagen biopolymeric matrices embedded with bimetallic Fe3O4@TiO2 NPs was prepared with multifunctional properties for environmental remediation applications. Magnetic bimetallic Fe3O4@TiO2 NPs were synthesized by mixing the pre-synthesized Fe3O4 NPs with titanium precursor followed by chemical reduction. Cellulose was extracted from Kenaf fibers (Kenaf fiber cellulose, KFC) whereas collagen was extracted from cowhide trimming wastes and combined to form a Kenaf fiber cellulose–collagen (KFCC) matrix. Combining BFT with KFCC yielded bio-based Kenaf fiber cellulose–collagen nanocomposite sponge incorporated with BFT NPs (KFCC-BFT) was characterized for their structural and functional properties and further studied for wastewater remediation applications.

Kenaf fiber was extracted from the kenaf tree (cultivated traditionally by farmers for making ropes to tie piles of rice after harvest for storage) collected in Issakaha village, from the Korhogo region, Côte d’Ivoire (Ivory Coast). All the plant experiments were in compliance with relevant institutional, national and international guidelines and legislation. Freshly flayed hides was purchased from the local slaughterhouse, Chennai, India. Raw cowhide trimming wastes were collected from the leather processing unit at CSIR-Central Leather Research Institute, Chennai, India. Hide powder was prepared from raw cowhide trimming wastes and were treated using the conventional process to remove the unwanted hair and flesh based on our previous report37. All chemicals were of analytical grade and were used without any further purification. Chemicals used were sodium hydroxide (SD Fine Chem Limited, 98%), sodium chlorite (LOBA Chemie, 80%), sodium sulfite anhydrous (EMPARTA, 98%), acetic acid (SRL, 99.9%), acetone (SD Fine Chem Limited), citric acid, titanium (IV) isopropoxide (Sigma Aldrich, 97%), iron (II) sulphate (SD Fine Chem Limited, 99%), iron (III) sulphate (SD Fine Chem Limited, 75%), ammonia (Rankem), isopropanol (Qaligens, 70%), ethanol (Hayman, 100%) and nitric acid (SD Fine Chem Limited, 69–72%).

Kenaf fibers were dried and cut into small pieces. 20 g of dried fibers were boiled with 300 mL of 6% NaOH (w/v) for 1 h. The pre-treated fibers were washed and ground in a laboratory mixer for 3 min to produce pulp-like fibers. Then, the delignification process was carried out by bleaching the pulp-like fibers with 300 mL 0.7% (w/v) sodium chlorite at pH 4, adjusted with 5% acetic acid and boiled for 3 h. The partially lignin-free fiber residue was washed with distilled water to neutral pH. The neutralized fiber residue was boiled with 300 mL 5% (w/v) sodium sulfite for 5 h to remove the lignin completely as well as hemicellulose partially. The obtained holocellulose was boiled with 300 mL 17.5% (w/v) sodium hydroxide solution for 5 h to remove the hemicelluloses. The isolated cellulose was washed with distilled water until neutral pH and air-dried38.

The Fe3O4 NPs were synthesized by the co-precipitation method. Briefly, 250 mL of the Erlenmeyer flask containing 100 mL of 0.1 M FeCl3 and 100 mL of 0.05 M FeSO4.7H2O were stirred for 30 min at 60 °C. Then, 25% of ammonia solution was added drop by drop until the pH reaches 10, leading to dark yellow precipitate. The obtained Fe3O4 NPs were washed thoroughly with distilled water to neutral pH and separated using centrifugation for 20 min at 10,000 rpm. The purified NPs were dried in a hot air oven at 100 °C for 8 h and calcinated at 500 °C for 2 h under a nitrogen environment.

For the synthesis of TiO2 NPs using the sol − gel method, 5 mL of titanium (IV) isopropoxide was added to 20 mL of ethanol and the mixture was stirred at 500 rpm at 60 °C for 30 min. Then, a mixture of 20 mL of ethanol/water (1:1) and 2 mL of HNO3 (72%) was added dropwise. The resulting mixture was stirred at 1000 rpm for another 3 h at 100 °C to form a gel. The obtained product was centrifuged at 10,000 rpm for 20 min. The collected pellet was washed with distilled water and then with ethanol and kept at 100 °C in a hot air oven for 8 h and calcinated at 500 °C for 2 h under a nitrogen environment.

Magnetic bimetallic Fe3O4@TiO2 NPs were synthesized through the chemical reduction method. In this procedure, 5 mL of titanium (IV) isopropoxide was dissolved in 25 mL isopropanol. Subsequently, 0.2 g of the pre-synthesized Fe3O4 NPs were added under vigorous stirring at 600 rpm for 1 h at 80 °C. To this, 100 mL of 0.1 M citric acid solution was added dropwise under continuous stirring at 300 rpm for 3 h to yield brown color precipitate (magnetic bimetallic Fe3O4@TiO2 NPs). The obtained magnetic NPs were purified by centrifugation at 10,000 rpm for 20 min, washed with ethanol and kept at 100 °C in a hot air oven for 8 h and calcinated at 500 °C for 2 h under a nitrogen environment.

The weighed amount of organic fibers (collagen and kenaf fiber cellulose) in 1:1 proportion was dissolved in 90 mL of 0.5 M glacial acetic acid using a homogenizer (Ika, T25) at 4 °C for 10 min. The wt.% of magnetic BFT NPs was calculated based on the weight of the organic fibers and three bio-sponges were fabricated namely KFCC, KFCC-BFT5, and KFCC-BFT10 corresponding to 0, 5 and 10% (wt./wt.) of BFT in the mixture. The BFT was sonicated using Lark Probe Sonicator for 2 min and added to the organic collagen–cellulose mixture. The mixture was homogenized at 4 °C for 1 h and transferred into 12 well plates and kept in a freezer (− 40 °C) for 2 h. Then, frozen products were kept in a lyophilizer (Delvac freeze drier) for 24 h to obtain hybrid magnetic KFCC-BFT bio-sponges.

The photocatalytic activity of the hybrid bio-sponges was investigated by analyzing the degradation of water-soluble crystal violet (CV) dye under visible light and sunlight irradiation under ambient environmental conditions. The initial concentration of CV is 2.5 × 10−5 mol/L. The photodegradation reaction was carried out in a 100 mL glass beaker containing 30 mL of CV dye. Before the photodegradation reaction, the glass beaker containing 30 mL of CV dye and bio-sponge was stirred for 30 min in the dark to establish adsorption–desorption equilibrium. Then, the solution was irradiated using 200 W Hg (Xe) with a medium pressure lamp (66,454 Newport Oriel Instrument) at room temperature or exposed directly to sunlight at ambient temperature for 180 min at neutral pH. The glass beaker holding the sample was held 20 cm from the light source during the irradiation procedures. At regular intervals of 10 min, samples of up to 1 mL were taken out for UV–visible examination.

The oil adsorbency of the nanocomposite was determined according to ASTM: F726-12 method39. A weighed dry bio-sponge (m0) was placed in a beaker containing excess used motor oil and allowed to immerse for 15 min. Then, the sponge was removed and drained for 2 min and the wet weight was taken (m1). The oil adsorbency as the ratio of oil adsorbed to the dry sponge weight was calculated as below.

With m0 the initial dry sponge weight, m1 weight of the sponge at end of the oil test and m = (m1 − m0) net oil adsorbed. The recyclability and reusability performance of the hybrid bio-sponge was also investigated according to ASTM:F726-12 using the centrifugation method. The centrifugation was carried out at 5000 rpm for 5 min at 25 °C. Additionally, the bio-sponge was added to a petri dish containing excess distilled water and 0.5 g of used motor oil in order to test the sponge's ability to absorb oil from an oil–water mixture and track the sponge in a magnetic field. With the help of a strong magnet, the sponge was moved through the petri-dish for 15 min to adsorb the oil. Then, the sponge was removed and drained for 2 min and the adsorbed oil was squeezed out. Digital photographs were taken during each stage of the process.

The crystalline structure of TiO2, Fe3O4 and BFT NPs were examined by using a Rigaku Miniflex (II) desktop diffractometer with Ni filtered Cu Kα radiation source (λ = 1.5418 nm) in the angular range of 20° to 80° at goniometer speed of 5 °C /min at room temperature. To identify the phase of the samples, XRD results were uploaded to the Joint Committee on Powder Diffraction Standards (JCPDS) software and the report was generated. The average crystallite d-size of NPs was determined using Debye–Scherrer Equation.

where, k represents the constant (0.89), λ stands for the wavelength of X-ray (1.5418 nm), β denotes full width at half the maximum of the diffraction peak and θ is the Bragg angle. Dynamic light scattering measurements (DLS) of the prepared NPs were analyzed using Zetasizer Nano ZS, series ZEN 3600, Malvern Instruments to obtain the particle size. UV–vis spectra of the NPs were obtained using a UV–visible spectrophotometer (Shimadzu UV-1800). The spectrum was taken from 200 to 800 nm with a 0.5 nm scanning interval. UV–vis diffusion reflectance spectra (UV–vis DRS) of bimetallic NPs and bio-sponges were obtained in a UV–Vis–NIR spectrophotometer (Agilent technologies) to determine the band gap energy.

The morphologies of the samples were examined with a field emission scanning electron microscope (FESEM, TESCAN, model-CLARA, Czech Republic) equipped with an energy-dispersive X-ray (EDX) spectroscopy. For high-resolution transmission electron microscopy (HRTEM, JEOL JEM 3010) analysis of BFT NPs, 5 µL of the sample was dispersed in 1 mL HPLC grade ethanol using water bath sonication for 30 min and 20 µL of the dispersed NPs was coated over the copper grid and dried at room temperature. The sample was observed at 200 kV voltage using LaB6 filament. To analyze the surface compositions of the nanocomposites, X-ray photoelectron spectroscopy (XPS) was performed using the ESCALAB 250 xi, Thermo Scientific. While pore size and pore diameter were determined using the Barrett–Joyner–Halenda (BJH) approach, the surface area was estimated using the Brunauer–Emmett–Teller (BET) theory. Fourier-transformed infrared (FT-IR) spectroscopic analysis was carried out using a Jasco spectrometer (Model No-4700) for the extracted cellulose, collagen, and synthesized bio-sponge samples. The surface wettability of sponges was characterized by water contact angle and oil (hexadecane) contact angle with a 5µL droplet. The measurements were obtained with a contact angle meter (Holmar, series HO-IAD-CAM-01) at room temperature. The magnetic properties of BFT, KFCC-BFT5 and KFCC-BFT10 were measured at room temperature using a vibrating sample magnetometer (VSM, Lakshore VSM 7410S).

Figure 1 shows the XRD patterns of the synthesized NPs. The diffraction peaks at 2θ angles of 25.4°, 37.8°, 48.1°, 54.1°, 55.3°, 62.9°, 68,7°, 70.5° and 75.3° can be assigned to the (101), (004), (200), (105), (211), (204), (116), (220) and (215) crystal planes of the anatase TiO2 phase (JCPDS No.021-1272)40. The magnetite NPs exhibit diffraction peaks at 2θ angles of 30.2°, 35.6°, 43.3°, 53.7°, 57.5°, 62.9° and 74.5° corresponding to the (220), (311), (400), (422), (511), (440) and (533) crystal planes of cubic Fe3O4 phase (JCPDS No. 65-3107)41. The sharp and intense crystallinity peaks at 2θ angles of 25.4° and 35.6° corresponding to the (101) and (311) planes of TiO2 and Fe3O4, respectively are present in the diffraction pattern of magnetic BFT NPs along with all the other peaks of both the nanoparticles. Crystallite size of the Fe3O4 and TiO2 was calculated as 24 and 15 nm, respectively using Scherrer’s formula as given in Eq. 2. Furthermore, the interplaner spacing value was calculated as 0.25 and 0.34 nm, which was resulting from the intense peak of the Fe3O4 (311) plane and TiO2 (101) plane, respectively. However, it is interesting to note the intensity of the peaks corresponding to the Fe3O4 is lower than those of TiO2. This could be due to the higher amount of TiO2 present in the bimetallic NPs compared to the Fe3O4.

X-ray diffractograms of the synthesized nanoparticles namely (a) TiO2, (b) Fe3O4 and (c) magnetic BFT.

The morphology of the magnetic BFT NPs was investigated by HRTEM. Figure 2a shows randomly dispersed Fe3O4 NPs coated with the TiO2 NPs. The result suggests that the magnetic BFT NPs are in aggregated form in contact with one another rather than the typical core–shell configurations. The Fe3O4 and TiO2 particles present in the bimetallic NPs seem to in the order of 20–25 nm although they are in contact aggregates. The particle size range observed here is comparable to the pristine Fe3O4 and TiO2 NP crystallite size obtained from XRD data. The HRTEM image (Fig. 2b) indicates that the lattice interlayer spacing of Fe3O4 and TiO2 is 0.24 and 0.33 nm, respectively coinciding with the (311) and (101) planes of the respective oxides, as revealed by XRD patterns42. The average particle size of TiO2 NPs, Fe3O4 NPs and uncalcined BFT NPs measured through DLS is 41, 250 and 391 nm, respectively as shown in Figure S1. After calcination at 500 °C for 2 h, it seems that BFT NPs got agglomerated with the increase in particle size to 703 nm. Overall, the particle size observed by DLS is much larger than the values obtained by XRD and HRTEM owing to the interaction of water molecules on the NP surface during DLS measurement. The UV–Vis absorption spectra of pristine TiO2, Fe3O4 and BFT NPs are shown in Fig. 2c. The absorption band of pure TiO2 NPs is in the range of 300–350 nm, which is in the UV region, while the magnetite Fe3O4 NPs exhibit the absorption band at 350–450 nm between UV and visible regions. In contrast, it should be noted that the BFT NPs are characterized by a wide band between 350 and 530 nm, which appears relatively high absorption in the visible region (400–800 nm). The addition of magnetite moiety induces a red shift in the absorption edges to a longer wavelength compared to pristine TiO2. Fe3O4 promotes the movement of electrons from the valence band to the conduction band, thus leading to a shift in TiO2 absorption in the range of its photocatalytic response5,17.

(a) Low and (b) high magnification HRTEM images of the magnetic BFT NPs. Lattice interlayer spacings originated by the (101) crystal planes of TiO2 and (311) crystal planes of Fe3O4 are clearly observable in the high magnification HRTEM image. (c) UV–vis spectra of pristine and BFT NPs and (d) M-H curves of BFT10 (powder Fe3O4@TiO2) and hybrid bio-sponges (KFCC-BFT5, KFCC-BFT10) analyzed using VSM.

Bimetallic NPs and magnetic hybrid organic–inorganic bio-sponges were characterized for their magnetic behavior using room temperature magnetization by VSM. Figure 2d shows typical S-like curves with perfect saturation magnetization indicating the ferromagnetic behavior of the bimetallic NPs and the bio-sponges. Compared to pure BFT NPs (with a saturation magnetization of 8.60 emu/g), the saturation magnetization values of bio-sponges were reduced to 1.44 and 0.86 emu/g, respectively for KFCC-BFT10 and KFCC-BFT5 nanocomposites as a function of dosage of BFT. The hysteresis loops are shown in Figures S2a and b. It is seen that both the pure BFT NPs and bio-sponges exhibit coercivity of about 118 Oe. Whereas the remanent magnetization for the BFT NPs is about 1.4 emu/g and 0.16 and 0.24 emu/g for the KFCC-BFT5 and KFCC-BFT10 nanocomposites, respectively, which behaves similar to the saturation magnetization trend.

FTIR spectrum of the extracted cellulose from kenaf fiber is shown in Fig. 3a. The band at 3336 cm−1 is attributed to the O–H stretching vibration and hydrogen bond of the hydroxyl groups. The band at 2889 cm−1 is the characteristic peak for alkanes exhibiting C–H stretching vibration of CH and CH2 asymmetric stretching in the cellulose backbone. The adsorbed water binding H–O–H band is observed at 1636 cm−1. The absorption peak at 1341 cm−1 corresponds to CH3 deformation. The intense band, centered at 1031 cm−1 is associated with the C–O stretching modes of the hydroxyl and ether groups in the cellulose. The band at 900 cm−1 can be attributed to the presence of β-glycosidic linkages and the small peak at 666 cm−1 is associated with the C–OH out-plane bending. It is interesting to note the disappearance of characteristics peaks at 1725 cm−1 and 1505 cm−1 corresponding to C=O stretching vibration of the acetyl groups in the hemicelluloses and the C=C stretching of the benzene ring of the lignin, respectively, indicating successful removal of these components during the cellulose extraction process.

FT-IR spectra of (a) KFC, (b) Collagen, (c) KFCC, and (d) KFCC-BFT10.

The FT-IR spectrum of pristine collagen in Fig. 3b depicts the characteristics peaks including the amide I (C=O stretching) at 1664 cm−1, the amide II (N–H bending couple to C–N vibration) at 1546 cm−1, the amide III (C–N stretching and N–H bending) at 1244 cm−1, the amide A (C–N stretching and N–H bending vibration) at 3343 cm−1 and the amide B (C–H stretching) at 3081 cm−16. The KFCC bio-sponge spectrum shows (Fig. 3c) characteristic peaks for both pristine collagen and cellulose with few changes in some peaks. The broad band at 3343 cm−1 corresponds to the N–H stretching vibration of amide A of collagen changed as a sharp band and present at the lower wavelength of 3322 cm−1. This result suggests that the N–H group of collagen may be involved in hydrogen bonds43. Interestingly, the characteristics peaks of pristine collagen corresponding to the amide I group shifted from 1664 to 1644 cm−1, from 1546 to 1536 cm−1 for the amide II group, and the amide III group from 1244 to 1237 cm−1, thus, indicating a blue shift of 20 cm−1, 10 cm−1 and 7 cm−1, respectively. These downshifts indicate a possible hydrogen bond interconnection between N–H groups of collagen and the hydroxyl OH group of cellulose43.

In the FTIR spectrum (Fig. 3d) of the magnetic hybrid bio-sponge KFCC-BFT10, we can observe key characteristic peaks of pure collagen and cellulose. Meanwhile, new peaks are observed at 549, 583 and 660 cm−1 corresponding to Fe–O stretching vibration of magnetite Fe3O4, Ti–O, and O–Ti–O bonds, respectively5,12. The presence of oxide bond peaks in the bio-sponge indicates the successful incorporation of the metal nanoparticles in the organic sponge.

The surface morphology of the bio-sponges (Fig. 4a–c) shows a multi-layered sheath-like spongious architecture and a highly linked porous network structure when probed through FESEM (Fig. 4a–c). It is clearly shown from the insert images (5 μm) that the hybrid bio-sponges (Fig. 4b and c) depict relatively dense and compact structures compared to the pristine KFCC bio-sponge (Fig. 4a). Further, it can be seen from Fig. 4c that the bimetallic Fe3O4@TiO2 NPs are tightly anchored to the surface and interior of the bio-sponge fibers possibly through hydrogen bond interaction with Fe–OH or Ti–OH25. In comparison to the KFCC bio-sponge (Fig. 4d), the EDX mapping images show that both organic (C, N, O) and inorganic (Ti, Fe) elements are present in the hybrid bio-sponges (Fig. 4e,f). To investigate the elemental composition, a selected region of the SEM image was taken and the EDX spectral analysis was carried out. EDX spectra results displayed in Figure S3a–c confirm the presence of Fe and Ti in the KFCC–BFT nanocomposites. The presence of C, N and O peaks indicates the main elements in the KFCC (Kenaf fiber and collagen) as shown in Figure S3a. As can be seen, the intensity of the Fe and Ti peaks is higher in the KFCC-BFT10 nanocomposite (Figure S3c) when compared to KFCC-BFT5 (Figure S3b) corresponding to the dosage of the BFT. There were no other peaks in the spectra that may be attributed to contaminants. These findings prove the high adhesion of Fe and Ti-based bimetallic nanoparticles to the KFCC surface.

FESEM images of as-synthesized (a) KFCC, (b) KFCC-BFT5 and (c) KFCC-BFT10 bio-sponges and inserts show magnified KFC-BFT5 and KFC-BFT10 sponges at 5 μm scale. Elemental mapping micrographs of as-synthesized (d) KFCC, (e) KFCC-BFT5 and (f) KFCC-BFT10 bio-sponges.

The N2 adsorption–desorption technique was employed to investigate the pore size, pore diameter and pore volume of the KFCC-BFT10 bio-sponge. As shown in Fig. 5a, KFCC-BFT10 bio-sponge exhibited characteristic hysteresis loop in the adsorption–desorption isotherm. According to IUPAC classification, the N2 adsorption–desorption isotherm of the KFCC-BFT10 bio-sponge show type IV isotherm pattern with H3 hysteresis loop, which means that the KFCC-BFT10 bio-sponge belongs to typical mesoporous material. The KFCC-BFT10 bio-sponge possesses a specific surface area of 40.9 m2/g according to Brunauer–Emmett–Teller (BET). Pore size distribution of the KFCC-BFT10 bio-sponge (Fig. 5b) shows two maxima. A very narrow peak at 2.2 nm and a broad pore size distribution from 3 to 6 nm indicate fairly wide distribution of pores. The prepared KFCC-BFT10 bio-sponge shows pore volume of 0.042 cm3/g (Fig. 5c). The high surface area and pore volume obtained may provide adequate surface sites for increased photocatalytic activity and oil sorption.

(a) BET plot (N2 adsorption–desorption isotherm) for KFCC-BFT10 bio-sponge, (b) BJH pore size distribution plot for KFCC-BFT10 bio-sponge. (c) BJH pore volume plot for KFCC-BFT10 bio-sponge.

The chemical composition and electronic structure of the developed photocatalyst were determined by the XPS spectra. The XPS survey spectra of KFCC, BFT and KFCC-BFT10 bio-sponge are illustrated in Fig. 6a and the core level spectra of Fe 2p and Ti 2p are shown in Fig. 6b–e. As can be seen in Fig. 6a, Fe 2p, Ti 2p, C 1s, N 1s, O 1s, and O 2s peaks are visible in the spectra of pristine BFT, KFCC and KFCC-BFT10 bio-sponge. These elemental compositions obtained for the nanoparticles, hybrid biopolymer matrix and nanocomposites through XPS analysis are concurrent with the FESEM − EDX data and further confirm that the samples are devoid of any impurities. The pristine BFT and KFCC-BFT10 bio-sponge showed two distinctive peaks of Fe3+ 2p3/2 and Fe3+ 2p1/2 in the Fe 2p spectra at 710.6 and 724.1 eV, respectively (Fig. 6b and c). It shows that the predominant form of Fe species in the nanocomposites is Fe3+ state. Additionally, the binding energies at 713.7 and 718.4 eV in the Fe 2p spectra of pure BFT could be attributed to Fe3+ in the spinel structure and the binding energy at 727.4 eV could be attributed to Fe3+ bound with a hydroxyl group. However, the binding energy in the Fe 2p spectra of the KFCC-BFT10 bio-sponge is slightly changed to 713.4, 719.0, and 727.5 eV, respectively. This meant that in the KFCC-BFT10 bio-sponge, the electrons could have more influence towards Fe3+. In the Ti 2p core level spectra of the pristine BFT10 and KFCC-BFT10 bio-sponge (Fig. 6d and e), two unique peaks at 458.4 and 464.3 eV are seen, which are attributed to Ti 2p3/2 and Ti 2p1/2, respectively, indicating that the titanium is mainly presented as Ti4+ in the anatase TiO2 form. This is in concurrence with our XRD data and also various literature values44,45. Thus, it is determined that Fe in Fe3O4@TiO2 has an oxidation state of + 3, whereas Ti is present as tetravalent and therefore both the Fe3+ and Ti4+ are in oxide form rather than in pure metallic form. The O 1s core level XPS spectra of pristine BFT, KFCC and KFCC-BFT10 bio-sponges are shown in Fig. 7. The binding energy range for the O 1s peak is 528–534 eV. Oxygen can exist in two different molecular states namely O2− and O2− with binding energy values of about 530 and 531.5 eV, respectively. For KFCC and KFCC-BFT10 bio-sponge, the O 1s peak appears at 530.7 and 531.5 eV, respectively. This component typically results from surface oxygen that is non-stoichiometric or OH from air. The surface O2 present in the oxides is responsible for the existence of a peak at 532.2 eV. In the case of BFT, two peaks are observed in the core-level spectra of O 1s. The low binding energy component observed at 529.7 eV is attributed to the O2− forming oxide whereas the peak at 530.8 eV is assigned to OH−. As can be seen, XPS data show that iron is present in the chemical state of Fe3+ and oxygen is predominantly in the state of O2−, thereby verifying the formation of Fe2O3. In brief, the Fe element in the KFCC-BFT10 bio-sponge is more positively charged, which would help in the regeneration of Fe3+ and thus may stimulate the photocatalytic degradation reaction.

(a) XPS survey spectra of KFCC, BFT and KFCC-BFT10 bio-sponge. The Fe 2p core level deconvoluted XPS spectra of (b) BFT and (c) KFCC-BFT10. The Ti 2p core level deconvoluted XPS spectra of (d) BFT and (e) KFCC-BFT10.

O 1s core level deconvoluted XPS spectra of (a) BFT, (b) KFCC and (c) KFCC-BFT10 bio-sponge.

The band gap energy of as-prepared bio-sponges was also investigated. From Fig. 8a, it is seen that the band gap energy of collagen and KFCC sponges are similar around ~ 5.1 eV and much higher than that of the hybrid KFCC-BFT10 bio-sponge, which is ~ 2.5 eV. It is seen that the band gap energy of bio-sponge without bimetallic nanoparticles is double the band gap energy of KFCC-BFT10. The possible reason for the decrease in band gap energy could be the effective interactions of Ti–O–Fe bonds in the KFCC matrix5,17. This reduced bandgap energy along with the red-shifted absorption in the visible region indicates that the hybrid KFCC-BFT10 bio-sponge can be excited under visible light or direct sunlight illumination to produce more electron–hole pairs for enhanced photocatalytic degradation activity of organic pollutants.

(a) UV–visible diffuse reflectance spectra of collagen, KFCC, KFCC-BFT5 and KFCC-BFT10 bio-sponges. Water contact angle of hybrid (b) KFCC-BFT5 and (c) KFCC-BFT10 bio-sponges.

The water contact angles of the hybrid bio-sponges are shown in Fig. 8b and c and relatively high water contact angle values were achieved after the interaction with the bimetallic nanoparticles. As the percentage of bimetallic NP in the sponge increases, the water contact angle also increases. This finding suggests that the as-prepared bio-sponges are reasonably hydrophobic. On the other hand, during the oil contact angle measurement, the oil droplet penetrated quickly into the hybrid bio-sponges and the contact angle could not be recorded. The wettability tests prove that the hybrid bio-sponges exhibit selective wettability towards water and oil. These hybrid bio-sponges can easily adsorb oil and repel water. The water contact angle for the pristine collagen–cellulose (KFCC) sponge could not be recorded because the water droplet was immediately absorbed by the sponge due to the hydrophilic property of cellulose and collagen.

As-prepared bio-sponges were used to study the degradation of aqueous crystal violet (CV) dye under visible light and sunlight in the presence of H2O2. Hydrogen peroxide plays a vital role in the degradation of CV by the generation of two strong hydroxyl radicals (HO·)46,47,48. The mechanism for the degradation of CV in presence of magnetic bimetallic Fe3O4@TiO2 NPs has been described by Vinosel et al.5 As seen in Fig. 9a, the adsorption capacity of the bio-sponge is primarily responsible for the removal of roughly 12.4% of the CV in 30 min under dark conditions, which was realised until adsorption equilibrium is established. It is observed that the sharpness and the intensity of the maximum absorption peak of CV at 590 nm decreased with extended visible illumination time followed by slight blue-shifting for the samples treated with KFCC-BFT5 and KFCC-BFT10 bio-sponges (Fig. 9b and c).

Photocatalytic degradation of crystal violet with (a) KFCC-BFT10 in dark condition, (b) KFCC-BFT5 and (c) KFCC-BFT10 in visible light irradiation and (d) KFCC-BFT10 under sunlight irradiation.

The photocatalytic degradation efficiency of CV dye under visible light irradiation is 85.4 and 91.2% for KFCC-BFT5 and KFCC-BFT10 bio-sponges, respectively. After 1 h of irradiation (Fig. 10a), about 50% of CV dye has been degraded and more than 60% dye in the case of KFCC-BFT10 bio-sponge. The hybrid KFCC-BFT10 bio-sponge photocatalyst shows greater degradation efficiency of 91.2% compared to 86% using 500 mg of pure Fe3O4@TiO2 powder photocatalyst in 500 mL water as reported by Vinosel et al.5 As can be seen, KFCC-BFT10 bio-sponge exhibited higher degradation capability owing to the higher BFT content and hence further subjected to photocatalytic degradation under sunlight exposure. The results demonstrate 86.6% degradation of CV dye for KFCC-BFT10 bio-sponge under sunlight (Fig. 9d). As shown in Table 1, the photocatalytic degradation of the KFCC-BFT10 bio-sponge photocatalyst synthesised in this study is comparable to other similarly reported photocatalysts with the added advantage of easy biodegradability of the photocatalyst support. The better photocatalytic degradation obtained with KFCC-BFT10 bio-sponge can be explained by the 3D macroporous structure and the floatability behavior (low density ~ 9 mg.cm−3), which provide the photocatalyst the ability to ease photocatalytic oxygenation activity in the air–water interface with high induced photon and increased interaction between the hybrid magnetic NPs catalyst and CV dye due to the presence of BFT on the surface as well as the inner layers of the bio-sponge support.

(a) Degradation rate of crystal violet dye as a function of time. (b) Oil sorption capacity of bio-sponge and (c) Digital photographs demonstrating the removal of oil using the hybrid bio-sponge from oil–water mixture. (d) Recyclability of the hybrid bio-sponge for oil removal.

To evaluate the sorbent performance characteristic of bio-sponge as a bio-based, easily biodegradable and eco-friendly material for oil spill removal (Fig. 10b–d), the oil adsorption capacity was investigated. From Fig. 10b, it is clearly seen that both hybrid bio-sponges exhibit a higher adsorption capacity of 41.4 and 46.1 g/g for KFCC-BFT5 and KFCC-BFT10 bio-sponges, respectively, compared to KFCC bio-sponge (37.2 g/g). This high adsorption capacity of the hybrid sponge can be corroborated by its 3D macroporous network structure and hydrophobicity. An added advantage of the developed magnetic hybrid bio-sponge is the ability to track the motion of the sponge on the surface of oil–water emulsion under a magnetic field (Fig. 10c). It is well established that the oil sorption capacity of a sorbent is mainly governed by some physical sorption properties such as the capillary effect due to the porous structure, van der Waals forces and the hydrophobic interactions between the sorbent and oils54, and in the present case the tracking under magnetic field is considered as an additional factor that controls the adsorption capacity of sorbent.

The recyclability and reusability of sorbent after oil removal is an important aspect to be considered during the evaluation of performance characteristics of an adsorbent such as adsorption capacity after repeating cycles of adsorbing-removing and waste management of the sorbent after being used in the environment. The as-prepared sponges are green and easily biodegradable and thus waste management after use can be done naturally without causing any harm to human beings and the environment. The recyclability and reusability data reveal that the hybrid bio-sponge exhibits high sorption capacity even after 5 cycles, showing only a small decrease from 46.1 g/g to around 40 g/g, after which the oil sorption efficiency decreases up to around 30 g/g and remains relatively constant up to 9 cycles (Fig. 10d). During recycling, it has been noticed that the hybrid bio-sponge still contains trapped oil rendering it sticky, highly packed, and dense material after centrifugation. After each cycle, the sponge was immersed in ethanol solution 2 times for 1 h, freeze-dried and lyophilized for 24 h. Figure 10c shows that the adsorbed oil may be easily removed by squeezing out and only a small amount of oil is left in the KFCC-BFT10 nanocomposite. The KFCC-BFT10 nanocomposite could be easily separated from the oil/water mixture by forceps and used for the next run thereby demonstrating its potential for oil removal applications with recyclability.

In summary, an easily biodegradable collagen–cellulose-based magnetic bio-sponge loaded with bimetallic Fe3O4@TiO2 NPs was fabricated with high potency for dye and oil removal. The structural morphology analysis by HRTEM revealed no core–shell structure but the deposition of TiO2 nanoparticles onto the surface of magnetite Fe3O4 nanoparticles. From room temperature magnetization measurement, it is found that the saturation magnetization value of bio-sponge was decreased compared to the value of pure BFT NPs and hysteresis loops with an S-like curve indicating ferromagnetic behavior of the bimetallic nanoparticles and bio-sponge. The morphology of the magnetic hybrid bio-sponge showed a 3D macroporous interconnection network with the BFT NPs bound on the surface and interior of the collagen–cellulose fibrous network as visualized through HRSEM. The wettability tests proved that the incorporation of the bimetallic NPs enhanced the hydrophobicity and roughness of the hybrid bio-sponges. The as-prepared bio-sponge exhibited high photodegradation activity by the removal of crystal violet dye up to 91.2 and 86.6% under visible light and direct sunlight irradiation, respectively. It is also demonstrated that a high oil sorption capacity of 46.1 g/g was achieved and the bio-sorbent can be recycled and reused up to 9 cycles. Based on the results, the as-prepared magnetic hybrid bio-sponge has a dual potential ability in wastewater remediation for dye removal and oil spill management thereby suggesting effective visible-light-driven photocatalytic application at an industrial scale.

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.

Zhang, M. et al. Efficient removal of organic pollutants by metal–organic framework derived Co/C yolk–shell nanoreactors: Size-exclusion and confinement effect. Environ. Sci. Technol. 54, 10289–10300 (2020).

Article ADS CAS PubMed Google Scholar

Li, X., Jia, Y., Zhou, M., Su, X. & Sun, J. High-efficiency degradation of organic pollutants with Fe, N co-doped biochar catalysts via persulfate activation. J. Hazard. Mater. 397, 122764 (2020).

Article CAS PubMed Google Scholar

Chen, D. et al. Photocatalytic degradation of organic pollutants using TiO2-based photocatalysts: A review. J. Clean. Prod. 268, 121725 (2020).

Article CAS Google Scholar

Wang, Z., Wu, A., Colombi Ciacchi, L. & Wei, G. Recent advances in nanoporous membranes for water purification. Nanomaterials 8, 65 (2018).

Article CAS PubMed PubMed Central Google Scholar

Vinosel, V. M. et al. Preparation and performance of Fe3O4/TiO2 nanocomposite with enhanced photo-Fenton activity for photocatalysis by facile hydrothermal method. Appl. Phys. A 125, 1–13 (2019).

Article Google Scholar

Nagaraj, S., Cheirmadurai, K. & Thanikaivelan, P. Visible-light active collagen-TiO2 nanobio-sponge for water remediation: A sustainable approach. Clean. Mater. 1, 100011 (2021).

Article CAS Google Scholar

Hernandez-Maya, R., Solís-López, M. & Th-Th, C. Photocatalytic degradation of orange G using TiO2/Fe3O4 nanocomposites. J. Mater. Sci. 29, 15436–15444 (2018).

Google Scholar

Pei, M. et al. State of the art of tertiary treatment technologies for controlling antibiotic resistance in wastewater treatment plants. Environ. Int. 131, 105026 (2019).

Article CAS PubMed Google Scholar

Ahmed, S. et al. Recent developments in physical, biological, chemical, and hybrid treatment techniques for removing emerging contaminants from wastewater. J. Hazard. Mater. 416, 125912 (2021).

Article CAS PubMed Google Scholar

Crini, G. & Lichtfouse, E. Advantages and disadvantages of techniques used for wastewater treatment. Environ. Chem. Lett. 17, 145–155 (2019).

Article CAS Google Scholar

Huang, X.-H. et al. Transparent floatable magnetic alginate sphere used as photocatalysts carrier for improving photocatalytic efficiency and recycling convenience. Carbohydr. Polym. 254, 117281 (2021).

Article CAS PubMed Google Scholar

Fan, H. et al. Facile synthesis of uniformly loaded Fe3O4–TiO2/RGO ternary hybrids for enhanced photocatalytic activities. Opt. Mater. 111, 110582 (2021).

Article CAS Google Scholar

Ahmed, A. et al. Efficient photocatalytic degradation of toxic Alizarin yellow R dye from industrial wastewater using biosynthesized Fe nanoparticle and study of factors affecting the degradation rate. Photochem. Photobiol. B Biol. 202, 111682 (2020).

Article CAS Google Scholar

Hajipour, P. et al. Surface modification of TiO2 nanoparticles with CuO for visible-light antibacterial applications and photocatalytic degradation of antibiotics. Ceram. Int. 47, 33875–33885 (2021).

Article CAS Google Scholar

Tekin, D., Birhan, D. & Kiziltas, H. Thermal, photocatalytic, and antibacterial properties of calcinated nano-TiO2/polymer composites. Mater. Chem. Phys. 251, 123067 (2020).

Article CAS Google Scholar

Charitha, T. et al. Efficient photodegradation activity of α-Fe2O3/Fe2TiO5/TiO2 and Fe2TiO5/TiO2 nanocomposites synthesized from natural ilmenite. Results Mater 12, 100219 (2021).

Article CAS Google Scholar

Chang, J., Zhang, Q., Liu, Y., Shi, Y. & Qin, Z. Preparation of Fe3O4/TiO2 magnetic photocatalyst for photocatalytic degradation of phenol. J. Mater. Sci. 29, 8258–8266 (2018).

CAS Google Scholar

Krishnan, S. & Shriwastav, A. Application of TiO2 nanoparticles sensitized with natural chlorophyll pigments as catalyst for visible light photocatalytic degradation of methylene blue. J. Environ. Chem. Eng. 9, 104699 (2021).

Article CAS Google Scholar

Parvate, S. et al. Titanium dioxide nanoparticle-decorated polymer microcapsules enclosing phase change material for thermal energy storage and photocatalysis. ACS Appl. Polym. Mater. 3, 1866–1879 (2021).

Article CAS Google Scholar

Liu, X. et al. The intrinsic effects of oxygen vacancy and doped non-noble metal in TiO2 (B) on photocatalytic oxidation VOCs by visible light driving. J. Environ. Chem. Eng. 10, 107390 (2022).

Article CAS Google Scholar

Chu, A.-C., Sahu, R. S., Chou, T.-H. & Shih, Y.-H. Magnetic Fe3O4@TiO2 nanocomposites to degrade bisphenol A, one emerging contaminant, under visible and long wavelength UV light irradiation. J. Environ. Chem. Eng. 9, 105539 (2021).

Article CAS Google Scholar

Yu, L. et al. In situ controllable fabrication of two-dimensional magnetic Fe3O4/TiO2@ Ti3C2T x composites for highly efficient phosphopeptides enrichment. ACS Appl. Mater. Interfaces 13, 54665–54676 (2021).

Article CAS PubMed Google Scholar

Chishti, A. N. et al. Synthesis of highly efficient and magnetically separable Fe3O4@ C-TiO2-Ag catalyst for the reduction of organic dyes and 4-nitrophenol. Colloids Surf. A 631, 127694 (2021).

Article CAS Google Scholar

Thanikaivelan, P., Narayanan, N. T., Pradhan, B. K. & Ajayan, P. M. Collagen based magnetic nanocomposites for oil removal applications. Sci. Rep. 2, 1–7 (2012).

Article Google Scholar

Peng, H. et al. Preparation of superhydrophobic magnetic cellulose sponge for removing oil from water. Ind. Eng. Chem. Res. 55, 832–838 (2016).

Article CAS Google Scholar

Peng, B. et al. Cellulose-based materials in wastewater treatment of petroleum industry. Green Energy Environ. 5, 37–49 (2020).

Article Google Scholar

Zhao, X.-Q., Wahid, F., Cui, J.-X., Wang, Y.-Y. & Zhong, C. Cellulose-based special wetting materials for oil/water separation: A review. Int. J. Biol. Macromol. 185, 890–906 (2021).

Article CAS PubMed Google Scholar

Yang, S. et al. Facile and sustainable fabrication of high-performance cellulose sponge from cotton for oil-in-water emulsion separation. J. Hazard. Mater. 408, 124408 (2021).

Article CAS PubMed Google Scholar

Meng, X., Dong, Y., Zhao, Y. & Liang, L. Preparation and modification of cellulose sponge and application of oil/water separation. RSC Adv. 10, 41713–41719 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Ahankari, S., Paliwal, P., Subhedar, A. & Kargarzadeh, H. Recent developments in nanocellulose-based aerogels in thermal applications: a review. ACS Nano 15, 3849–3874 (2021).

Article CAS PubMed Google Scholar

Ahuja, D. et al. Superhydrophobic modification of cellulose sponge fabricated from discarded jute bags for oil water separation. J. Environ. Chem. Eng. 9, 105063 (2021).

Article CAS Google Scholar

Pezzoli, D. et al. Fibronectin promotes elastin deposition, elasticity and mechanical strength in cellularised collagen-based scaffolds. Biomaterials 180, 130–142 (2018).

Article CAS PubMed Google Scholar

Curtin, C. et al. A physiologically relevant 3D collagen-based scaffold–neuroblastoma cell system exhibits chemosensitivity similar to orthotopic xenograft models. Acta Biomater. 70, 84–97 (2018).

Article CAS PubMed Google Scholar

Ramanathan, G. et al. Fabrication of biohybrid cellulose acetate-collagen bilayer matrices as nanofibrous spongy dressing material for wound-healing application. Biomacromol 21, 2512–2524 (2020).

Article CAS Google Scholar

Kalirajan, C. & Palanisamy, T. Bioengineered hybrid collagen scaffold tethered with silver-catechin nanocomposite modulates angiogenesis and TGF-β toward scarless healing in chronic deep second degree infected burns. Adv. Healthc. Mater. 9, 2000247 (2020).

Article CAS Google Scholar

Zhang, S. et al. Construction and nanostructure of chitosan/nanocellulose hybrid aerogels. Biomacromol 22, 3216–3222 (2021).

Article CAS Google Scholar

Nagaraj, S., Easwaramoorthi, S., Rao, J. R. & Thanikaivelan, P. Probing visible light induced photochemical stabilization of collagen in green solvent medium. Int. J. Biol. Macromol. 131, 779–786 (2019).

Article Google Scholar

Mandal, A. & Chakrabarty, D. Isolation of nanocellulose from waste sugarcane bagasse (SCB) and its characterization. Carbohydr. Polym. 86, 1291–1299 (2011).

Article CAS Google Scholar

Astm, F. Standard test method for sorbent performance of adsorbents. Annual Book of ASTM Standards. ASTM Committee on Standards West Conshohocken (1998).

Chalasani, R. & Vasudevan, S. Cyclodextrin-functionalized Fe3O4@TiO2: Reusable, magnetic nanoparticles for photocatalytic degradation of endocrine-disrupting chemicals in water supplies. ACS Nano 7, 4093–4104 (2013).

Article CAS PubMed Google Scholar

Lu, Z. et al. Enhanced recyclability, stability, and selectivity of CdS/C@ Fe3O4 nanoreactors for orientation photodegradation of ciprofloxacin. Chem. Eur. J. 21, 18528–18533 (2015).

Article ADS PubMed Google Scholar

He, J., Zeng, X., Lan, S. & Lo, I. M. Reusable magnetic Ag/Fe, N-TiO2/Fe3O4@SiO2 composite for simultaneous photocatalytic disinfection of E. coli and degradation of bisphenol A in sewage under visible light. Chemosphere 217, 869–878 (2019).

Article ADS CAS PubMed Google Scholar

Lohrasbi, S., Mirzaei, E., Karimizade, A., Takallu, S. & Rezaei, A. Collagen/cellulose nanofiber hydrogel scaffold: Physical, mechanical and cell biocompatibility properties. Cellulose 27, 927–940 (2020).

Article CAS Google Scholar

Ainali, N. M., Kalaronis, D., Evgenidou, E., Bikiaris, D. N. & Lambropoulou, D. A. Insights into biodegradable polymer-supported titanium dioxide photocatalysts for environmental remediation. Macromol 1, 201–233 (2021).

Article CAS Google Scholar

Liu, J. et al. Facet–activity relationship of TiO2 in Fe2O3/TiO2 nanocatalysts for selective catalytic reduction of NO with NH3: In situ DRIFTs and DFT studies. J. Phys. Chem. C 121, 4970–4979 (2017).

Article ADS CAS Google Scholar

Elmolla, E. S. & Chaudhuri, M. Photocatalytic degradation of amoxicillin, ampicillin and cloxacillin antibiotics in aqueous solution using UV/TiO2 and UV/H2O2/TiO2 photocatalysis. Desalination 252, 46–52 (2010).

Article CAS Google Scholar

Liu, J. et al. Photo-Fenton reaction and H2O2 enhanced photocatalytic activity of α-Fe2O3 nanoparticles obtained by a simple decomposition route. J. Alloys Compd. 771, 398–405 (2019).

Article CAS Google Scholar

Truong, H. B. et al. H2O2-assisted photocatalysis for removal of natural organic matter using nanosheet C3N4-WO3 composite under visible light and the hybrid system with ultrafiltration. J. Chem. Eng. 399, 125733 (2020).

Article CAS Google Scholar

de Oliveira Pereira, L. et al. Preparation of magnetic photocatalysts from TiO2, activated carbon and iron nitrate for environmental remediation. J. Photochem. Photobiol., A 382, 111907 (2019).

Article Google Scholar

Ravikumar, M. P. et al. Insights into the photocatalytic memory effect of magneto-plasmonic Ag–Fe3O4@TiO2 ternary nanocomposites for dye degradation and H2 production under light and dark conditions. Energy Fuels 36, 11503–11514 (2022).

Article CAS Google Scholar

Bibi, S. et al. Photocatalytic degradation of malachite green and methylene blue over reduced graphene oxide (rGO) based metal oxides (rGO-Fe3O4/TiO2) nanocomposite under UV-visible light irradiation. J. Environ. Chem. Eng. 9, 105580 (2021).

Article CAS Google Scholar

Hatefi, R., Younesi, H., Mashinchian-Moradi, A. & Nojavan, S. A facile decoration of anatase Fe3O4/TiO2 nanocomposite with graphene quantum dots: Synthesis, characterization, and photocatalytic activity. Adv. Powder Technol. 32, 2410–2422 (2021).

Article CAS Google Scholar

Shi, L., Wang, X., Hu, Y. & He, Y. Investigation of photocatalytic activity through photo-thermal heating enabled by Fe3O4/TiO2 composite under magnetic field. Sol. Energy 196, 505–512 (2020).

Article ADS CAS Google Scholar

Nguyen, S. T. et al. Cellulose aerogel from paper waste for crude oil spill cleaning. Ind. Eng. Chem. Res. 52, 18386–18391 (2013).

Article CAS Google Scholar

Download references

EFA acknowledges CSIR for awarding TWAS (CSIR-TWAS) postdoctoral fellowship. SN acknowledges CSIR for granting Senior Research Fellowship. Authors thank CSIR-CLRI for financial support through the MLP02 project on “Collagen and other protein-based innovative materials for heterogeneous applications”. The authors acknowledge the ICP, CSIR-CECRI for providing the XPS characterization facility. The authors thank CLRI-CATERS for the analysis facilities. CSIR-CLRI Communication Number 1795.

Advanced Materials Laboratory, CSIR-Central Leather Research Institute (CSIR-CLRI), Sardar Patel Road, Adyar, Chennai, 600 020, India

E. F. Assanvo, S. Nagaraj & P. Thanikaivelan

Laboratoire de Thermodynamique et de Physico-Chimie du Milieu, UFR SFA, Université Nangui Abrogoua, 02 BP 801, Abidjan 02, Côte d’Ivoire

E. F. Assanvo & D. Boa

University of Madras, Chepauk, Chennai, 600005, India

S. Nagaraj & P. Thanikaivelan

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

E.F.A. executed the major experiments. E.F.A. and S.N. wrote the main manuscript text and prepared all the figures. P.T. designed the work and edited the manuscript. All authors reviewed the manuscript.

Correspondence to P. Thanikaivelan.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Assanvo, E.F., Nagaraj, S., Boa, D. et al. Hybrid collagen–cellulose–Fe3O4@TiO2 magnetic bio-sponges derived from animal skin waste and Kenaf fibers for wastewater remediation. Sci Rep 13, 13365 (2023). https://doi.org/10.1038/s41598-023-40520-y

Download citation

Received: 06 January 2023

Accepted: 11 August 2023

Published: 17 August 2023

DOI: https://doi.org/10.1038/s41598-023-40520-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative